It is made of pure graphite sheet\/coiled material, and chemical and high temperature treated by natural high pure flake graphite, and die-pressed or rolling pressed, with no bonding adhesive. Under the brash working condition. It will still have a good sealing performance, with long lifespan, and low maintain cost.<\/P> Sheet Site<\/FONT><\/STRONG><\/TD><\/TR>Density(g\/cm3<\/SUP>)<\/P><\/TD>Length(mm)<\/P><\/TD> | Width(mm)<\/P><\/TD> | Thickness(mm)<\/TD><\/TR> | 0.7-1.2<\/TD> | <=1500<\/TD> | <=1500<\/TD> | 0.2-3.0<\/TD><\/TR><\/TBODY><\/TABLE><\/TD><\/TR> | <\/STRONG><\/TD><\/TR>Roll Size<\/STRONG><\/FONT><\/TD><\/TR>Density(g\/cm3<\/SUP>)<\/P><\/TD>Length(mm)<\/P><\/TD> | Width(mm)<\/P><\/TD> | Thickness(mm)<\/TD><\/TR> | 0.7-1.1<\/TD> | 30-100<\/TD> | <=1500<\/TD> | 0.2-0.8<\/TD><\/TR><\/TBODY><\/TABLE><\/TD><\/TR> | <\/STRONG><\/TD><\/TR>Service Range<\/FONT><\/STRONG><\/TD><\/TR>Temperature(¡ãC )<\/TD> | <\/TD> | <\/TD><\/TR> | In oxidizing atmosphere<\/P><\/TD> | In non-oxidizing atmosphere<\/P><\/TD> | Pressure (Mpa) <\/TD> | PH Range<\/P><\/TD><\/TR> | -240˜450<\/TD> | -240˜3500<\/TD> | 30<\/TD> | 0˜14<\/TD><\/TR><\/TBODY><\/TABLE><\/TD><\/TR> | <\/STRONG><\/TD><\/TR>Main Properties<\/FONT><\/STRONG><\/TD><\/TR>Project<\/TD> | I<\/TD> | II<\/TD><\/TR> | Tolerance of density ( g\/cm3 )<\/SUP><\/P><\/TD>¡À0.05<\/TD> | ¡À0.06<\/TD><\/TR> | Tolerance of thickness<\/TD> | ¡À0.03<\/TD> | ¡À0.04<\/TD><\/TR> | Carbon Contant ( % )<\/P><\/TD> | 99.8<\/TD> | 98<\/TD><\/TR> | Tensile Strength ( Mpa )<\/P><\/TD> | =>4.5<\/TD> | =>4.5<\/TD><\/TR> | Compressibility( % )<\/P><\/TD> | =>40<\/TD> | =>40<\/TD><\/TR> | Recovery( % )<\/P><\/TD> | =>10<\/TD> | =>10<\/TD><\/TR> | Sulphur Content( PPm )<\/P><\/TD> | <700<\/TD> | <1000<\/TD><\/TR> | Chlorine Content( PPm )<\/P><\/TD> | <25<\/TD> | <50<\/TD><\/TR> | Stress relaxation( % )<\/P><\/TD> | 10<\/TD> | 10<\/TD><\/TR> | lgnition Loss( % )<\/TD> | <0.5<\/TD> | <0.1<\/TD><\/TR><\/TBODY><\/TABLE><\/TD><\/TR><\/TBODY><\/TABLE><\/P><\/td><\/tr> | <\/td><\/tr> | <\/td><\/tr><\/table>");
| |
| | |
| | | |
| | | |
| |
|